Language

surface hardening

2022-06-17


Case hardening and tempering heat treatment is usually carried out by induction heating or flame heating. The main technical parameters are surface hardness, local hardness and effective hardened layer depth. Vickers hardness tester can be used for hardness testing, Rockwell or surface Rockwell hardness tester can also be used. The selection of the test force (scale) is related to the depth of the effective hardened layer and the surface hardness of the workpiece. There are three durometers involved here. 1. Vickers hardness tester is an important method to test the surface hardness of heat-treated workpieces. It can use a test force of 0.5-100kg to test the surface hardened layer as thin as 0.05mm thick. Its accuracy is yes, and it can distinguish the surface hardness of heat-treated workpieces. small differences. In addition, the depth of the effective hardened layer is also detected by a Vickers hardness tester. Therefore, it is necessary to have a Vickers hardness tester for units that perform surface heat treatment processing or use a large number of surface heat treatment workpieces. 2. The surface Rockwell hardness tester is also very suitable for testing the hardness of surface quenched workpieces. There are three scales for the surface Rockwell hardness tester to choose from. Various case-hardened workpieces with an effective hardening depth of more than 0.1mm can be tested. Although the accuracy of the surface Rockwell hardness tester is not as high as that of the Vickers hardness tester, it has been able to meet the requirements as a detection method for quality management and qualification inspection of heat treatment plants. Moreover, it also has the characteristics of simple operation, convenient use, low price, rapid measurement, and direct reading of hardness values. Using the surface Rockwell hardness tester, batches of surface heat-treated workpieces can be quickly and non-destructively tested piece by piece. This has important implications for metalworking and machine building plants. 3. When the surface heat treatment hardening layer is thick, the Rockwell hardness tester can also be used. When the thickness of the heat treatment hardened layer is 0.4-0.8mm, the HRA scale can be used, and when the thickness of the hardened layer exceeds 0.8mm, the HRC scale can be used. The three hardness values ​​of Vickers, Rockwell and superficial Rockwell can be easily converted to each other and converted into standard, drawing or user-required hardness value. The corresponding conversion table has been given in the international standard ISO, American standard ASTM and Chinese standard GB/T.

surface hardening

Case hardening and tempering heat treatment is usually carried out by induction heating or flame heating. The main technical parameters are surface hardness, local hardness and effective hardened layer depth. Vickers hardness tester can be used for hardness testing, Rockwell or surface Rockwell hardness tester can also be used. The selection of the test force (scale) is related to the depth of the effective hardened layer and the surface hardness of the workpiece. There are three durometers involved here. 1. Vickers hardness tester is an important method to test the surface hardness of heat-treated workpieces. It can use a test force of 0.5-100kg to test the surface hardened layer as thin as 0.05mm thick. Its accuracy is yes, and it can distinguish the surface hardness of heat-treated workpieces. small differences. In addition, the depth of the effective hardened layer is also detected by a Vickers hardness tester. Therefore, it is necessary to have a Vickers hardness tester for units that perform surface heat treatment processing or use a large number of surface heat treatment workpieces. 2. The surface Rockwell hardness tester is also very suitable for testing the hardness of surface quenched workpieces. There are three scales for the surface Rockwell hardness tester to choose from. Various case-hardened workpieces with an effective hardening depth of more than 0.1mm can be tested. Although the accuracy of the surface Rockwell hardness tester is not as high as that of the Vickers hardness tester, it has been able to meet the requirements as a detection method for quality management and qualification inspection of heat treatment plants. Moreover, it also has the characteristics of simple operation, convenient use, low price, rapid measurement, and direct reading of hardness values. Using the surface Rockwell hardness tester, batches of surface heat-treated workpieces can be quickly and non-destructively tested piece by piece. This has important implications for metalworking and machine building plants. 3. When the surface heat treatment hardening layer is thick, the Rockwell hardness tester can also be used. When the thickness of the heat treatment hardened layer is 0.4-0.8mm, the HRA scale can be used, and when the thickness of the hardened layer exceeds 0.8mm, the HRC scale can be used. The three hardness values ​​of Vickers, Rockwell and superficial Rockwell can be easily converted to each other and converted into standard, drawing or user-required hardness value. The corresponding conversion table has been given in the international standard ISO, American standard ASTM and Chinese standard GB/T.